Brushed , Anodized aluminium fan blade for motor 6082-T6 , 6005-T6 HHS5 manufacturer from China Hentec Industry Co.,Ltd.

Brushed , Anodized aluminium fan blade for motor 6082-T6 , 6005-T6

Place of Origin:

Zhejiang, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Model No.: HHS5

Descrition:

1. Item :Anodized Aluminum Fan Blades , 6063 / 6061 /6005</

Descrition:

1. Item :Anodized Aluminum Fan Blades , 6063 / 6061 /6005
2. Alloy temper: 6060-T66 6063-T5/T6 ; 6061-T5/T6 ; 6082-T6; 6005-T6
3. Standard: EN755, ASTMB221, DIN Standard
4. Surface treatment: Mill finish; Anodizing; Powder coated, Brushed.
5. Application: Construction; Car; Aerospace; Ship; Armarium; Industrial equipment; Woodworking machinery and etc.
6. Manufacturing Process: Die designing→ Die making→ Smelting& alloying→ Extruding→ Cutting→ CNC machining→ Driling→ Tapping→ Surface treatment→ Welding→ Assembling→ Packing

Alloy/Temper	6060-T66 6063-T5/T6 ; 6061-T5/T6 ; 6082-T6; 6005-T6
Surface treatment	Mill finishes; Anodized; Powder coated; Wooden grain, Machine/Acid polished and etc
Standard apply	EN755; DIN; ASTMB221; GB5237-2008 and etc.
Price	SMM/LME Primary aluminum price + the most competitive conversion cost
Mould policy	100%T/T in advance
Delivery timetable	sample: within 20 days; order: within 20 days
Payment term	30% deposit, the balance pay against B/L copy within 7 days
Packing standard	Protected film and pearl cotton inside and shrink film outside
Guarantee term	If the shipped products can not meet required, the total order amount will be refund back without delay, or arrange new replacement cargoes instead.

Specifications:
1. Primary Technical Data
1) Chemical composition

Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Impurity	Al
6063	0.2-0.6	0.35	0.1	0.1	0.45-0.9	0.1	0.1	0.1	0.15	Rest
6061	0.4-0.8	0.7	0.15-0.4	0.15	0.8-1.2	0.04-0.35	0.25	0.15	0.15	Rest
6060	0.3-0.6	0.1-0.3	0.1	0.1	0.35-0.6	-	0.15	0.1	0.15	Rest
6005	0.6-0.9	0.35	0.1	0.1	0.40-0.6	0.1	0.1	0.1	0.15	Rest

2) Mechanical property

Alloy	Temper	Tensile strength	Yield strength	Elongation
6063	T5	≥ 160Mpa	≥ 110Mpa	≥ 8%
6063	T6	≥ 205Mpa	≥ 180Mpa	≥ 8%
6061	T6	≥ 265Mpa	≥ 245Mpa	≥ 8%

3. Surface Treatment of Sections

(Class)	(μm),not diminish than		acid-resistant			abrasion resistance
	(Min-average film thickness)	(Min-part film thickness)	CASS		(S)
	(Min-average film thickness)	(Min-part film thickness)	(h)	Class	(S)	(f, g /μm)
AA10	10	8	16	≥9	≥50	≥300
AA15	15	12	32	≥9	≥75	≥300
AA20	20	16	56	≥9	≥100	≥300
AA25	25	20	72	≥9	≥125	≥300

Competitive Advantage:
6. Advantage:
1) Pure 99.7% aluminum materials without any scrap used
2) OEM welcome, we can design and cut die to meet customer's special demand
3) Wonderful surface treatment, we can meet customers required on surface
4) Strictly quality control process assured higher quality.
5) Hard Alloy Longer life span.
6) Packing safety and convenient.